Ni离子注入纯铜的表面改性
白亚奎,李杰池,郑瑞廷,程国安

(北京师范大学 低能核物理研究所 射线束技术与材料改性教育部重点实验室 北京市辐射中心,北京 100875)

摘 要: 采用MEVVA源离子注入设备进行了纯铜表面镍离子注入的改性实验研究,采用透射电镜和X射线衍射仪对改性层显微组织进行分析表征。结果表明:随着Ni离子注入剂量的增加,铜表面改性层发生一系列强化过程。纳米硬度和摩擦磨损实验结果表明:当注入剂量达到7.5×1017 ion/cm2时,注入层的硬度值可达基体的2倍,滑动摩擦因数仅为基体的47%。高剂量的离子注入是对纯铜进行表面改性的一种有效的方法。

 

关键字: 镍;铜;离子注入;表面改性

Surface modification of pure copper by Ni ion implantation
BAI Ya-kui, LI Jie-chi, ZHENG Rui-ting, CHENG Guo-an

Key Laboratory of Beam Technology and Material Modification of National Ministry of Education , Institute of Low Energy Nuclear Physics, Beijing Normal University, Beijing Radiation Center, Beijing 100875, China

Abstract:The impact on the surface of pure copper performance with Nickel ion implantation was studied using MEVVA source ion implantation equipment. The microstructures of modified layer were analyzed by TEM and XRD. The results show that a series of strengthening process occur on the modified surface of copper with the increase of Ni ion implantation dose on surface of copper. The testing results of hardness and friction indicate that the surface hardness is 2 times as that of original copper surface when the ion implanted dose is 7.5×1017 ion/cm2, and the friction coefficient is only 47% of that of copper surface. It can be concluded that ion implantation on the surface of pure copper, especially strong current ion implantation, is an effective method of pure copper surface strengthening technology.

 

Key words: Ni; Cu; ion implantation; surface modification

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com