Al基和Al-6Si基闭孔泡沫铝的动态压缩性能
尉海军,李 兵,郭志强,姚广春

(东北大学 材料与冶金学院,教育部材料先进制备技术工程研究中心,沈阳 110004)

摘 要:

利用熔体转移发泡法制备了不同密度的Al基和Al-6Si基闭孔泡沫铝(CCAF),探讨了CCAF基体的微观形貌及物相组成,对其动态压缩性能进行了研究。结果表明:Al基CCAF基体微观形貌较单一,基本上是小块状(Al20CaTi2);而Al-6Si基CCAF基体微观形貌复杂,主要呈大片状(Al3.21Si0.47和CaAl2Si3)、长针状(Al3Ti)和小白点(Al2O3)。动态压缩结果显示:Al基CCAF压缩应力—应变曲线较平缓,断裂层有明显的材料撕裂痕迹;而Al-6Si基CCAF压缩应力—应变曲线不光滑,个别曲线波动较大,断裂层出现显著的脆性材料断裂特征;随着相对密度的增加,Al基和Al-6Si基CCAF屈服强度(σpl)和表观弹性模量(E0.2)整体趋势都在增加。

 

关键字: 闭孔泡沫铝;动态压缩;相对密度;屈服强度;表观弹性模量

Dynamic compressive property of closed-cell
aluminum foam with Al matrix and Al-6Si matrix
YU Hai-jun, LI Bing, GUO Zhi-qiang, YAO Guang-chun

Engineering and Researching Centre of Advanced Preparation Technology of Materials, Ministry of Education,
School of Materials and Metallurgy, Northeastern University, Shenyang 110004, China

Abstract:Closed-cell aluminum foam (CCAF) with Al matrix and Al-6Si matrix was prepared by method of molten body transitional foaming process, the metallography of matrix was discussed, and its dynamic compressive property was researched. The results show that the metallography of CCAF with Al matrix is simple, basically existing as small pieces (Al20CaTi2), whereas the metallography of CCAF with Al-6Si matrix is complex, mainly existing as big pieces (Al3.21Si0.47 and CaAl2Si3), long needles (Al3Ti) and small white flakes (Al2O3). Dynamic compressive results display that the stress—strain curves of CCAF with Al matrix are smooth, the zone of fractures has obvious teared trace, whereas the stress—strain curves of CCAF with Al-6Si matrix are not smooth, certain curve fluctuates markedly, and zone of fracture indicates obvious fracture characteristic of brittle materials. With increasing relative density, the whole trend of yield strength (σpl) and apparent elastic modulus (E0.2) also increases.

 

Key words: closed-cell aluminum foam; dynamic compression; relative density; yield strength; apparent elastic modulus

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com