镍−磷−钛酸钾晶须化学复合镀层的制备及性能
金亚旭,华 林

(武汉理工大学 材料科学与工程学院,武汉 430070)

摘 要: 采用化学复合镀方法制备镍钛酸钾晶须复合镀层,用扫描电镜和金相显微镜观察复合镀层的表面形貌和断面结构,用XRD研究时效温度对镀层组织结构的影响,并解释时效温度对镀层显微硬度的影响机制。采用交流阻抗技术和中性盐雾实验研究镀层的耐腐蚀性能。在销盘式摩擦磨损试验机上进行复合镀层的摩擦磨损性能测试。结果表明:镀层的显微硬度随温度的变化曲线呈单峰形态,在400 时达到最大值;复合镀层具有良好的耐腐蚀性能和摩擦磨损性能,在同等实验条件下,复合镀层的磨损率只有Ni-P镀层的1/4

 

关键字: 钛酸钾晶须;化学复合镀;镀层性能

Preparation and properties of electroless composite plating of nickel-phosphous-potassium titanate whisker
JIN Ya-xu, HUA Lin

School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

Abstract:Nickel-phosphorus composite coatings containing potassium titanate whisker (PTW) were prepared by electroless plating. The surface morphology and cross-sectional microstructure of the coatings were investigated by scanning electron microscopy and optical metallographic microscopy. The effect of aging temperature on the microstructure of the coatings was studied by XRD, and the effect of aging temperature on microscopic hardness was analyzed. The corrosion behavior of the electroless coatings was examined by electrochemical impedance spectroscopy and neutral salt spray test. The tribological performances of coatings were evaluated by a pin-on-plate wear tester. The results show that the corrosion resistance of composite coating is improved significantly by incorporation of PTW. The composite coatings exhibit higher wear resistance. The wear rate of the composite coating is approximately one-fourth of that of Ni-P coating under the same conditions.

 

Key words: potassium titanate whisker; electroless composite plating; coating property

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com