Characterization of TiAl-based alloy with high-content Nb by powder metallurgy
SUN Hong-fei1, LI Xue-wen1, FENG Jie1, FANG Wen-bin1,2

1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
2. School of Materials Science and Engineering, Harbin University of Science and Technology,
Harbin 150040, China

Abstract:Powders with nominal composition of Ti-45Al-10Nb (mole fraction, %) were prepared by mechanical ball milling and were then consolidated by hot-pressed sintering in vacuum atmosphere. The microstructures of 12 h-milling composite powders and sintered bulk materials were characterized by OM, XRD, SEM and EDX. The results showed that the composite powders were completely homogeneous, and fine-grained Ti/Al/Nb composite powders were made. The microstructure of the consolidated alloy was composed of fine equiaxed grains with large pure Nb particles. And the results also indicated that the compressive strength and ductility of the sintered TiAl-based bulk material at RT could be improved effectively by adding 10% Nb element. The yield strength (σ0.2) and fracture strength (σb) of the alloy were 842 MPa and 1314 MPa, respectively, and the compressive ductility (δp) was 12.4%.

 

Key words: TiAl-based alloy; powder metallurgy; particle size; composites; sintered bulk

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com