中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 22 No. 12 December 2012 |
（1. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China;
2. School of Metallurgical Science and Engineering, Central South University, Changsha 410083, China）
Abstract:To protect carbon materials from oxidation, mullite/SiC coatings were prepared on graphite by chemical vapor reaction (CVR) and slurry sintering. The XRD analyses show that the phase of the outer-layer coating is composed of SiO2 and mullite, and the inner-layer coating is mainly composed of β-SiC. The anti-oxidation behavior of the coating and the Rockwell hardness (HRB) of the coating after oxidation were investigated. The oxidation test shows that the as-prepared multi-layer coating exhibits excellent anti- oxidation and thermal shock resistance at high temperature. After oxidation at 1150 °C for 109 h and thermal shock cycling between 1150 °C and room temperature for 12 times, the mass gain of the coated sample is 0.085%. Meanwhile, the indentation tests also demonstrate that the as-prepared coating has good bonding ability between the layers.
Key words: carbon materials; oxidation resistance; coating; SiC; mullite