Decarburization and improvement of
ultra fine straight WC−8Co sintered via microwave sintering
BAO Rui1, YI Jian-hong1,2, PENG Yuan-dong1, ZHANG Hao-ze1, LI Ai-kun1

1. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China;
2. School of Materials Science and Engineering, Kunming University of Science and Technology,
Kunming 650093, China

Abstract:Cemented tungsten carbide with ultra fine grains was prepared via microwave sintering. η phase (W3Co3C) was formed on the surface of the samples during the preparation process. Extra carbon black was premixed and the influence of carbon content on mechanical properties was studied. The results show that the maximum value of hardness and transverse rupture strength are HRA 93.2 and 3396 MPa respectively when the carbon black content is 0.45%. The microstructure investigated by SEM show that the WC grains growth mainly occurs during the early stage of microwave sintering by the coalescence of grains.


Key words: cemented carbide; microwave sintering; carbon content; mechanical properties

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱