中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
Vol. 22 No. 1 January 2012 |
stress corrosion cracking of 7085 aluminum alloy
(State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China)
Abstract:The influence of quenching rate on microstructure and stress corrosion cracking (SCC) of 7085 aluminum alloy was investigated by tensile test, slow strain rate test (SSRT), combined with scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical test. The results show that with decreasing the quenching rate, the size and inter-particle distance of the grain boundary precipitates as well as precipitation free zone width increase, but the copper content of grain boundary precipitates decreases. The SCC resistance of the samples increases first and then decreases, which is attributed to the copper content, size and distribution of grain boundary precipitates.
Key words: 7085 aluminum alloy; quenching rate; microstructure; stress corrosion cracking