中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
Vol. 21 Special 2 August 2011 |
(School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China)
Abstract:Al2O3/Ni-Co composites with different additives and Al2O3 particles were fabricated by pulse current electrodeposition. The effects of different additives and Al2O3 particles on the surface smoothness, micro-hardness and plastic deformation at room temperature and high temperature were compared. Scanning electron microscopy was employed to examine the microstructures of the as-deposited and deformed samples. The hardness, fracture strength at room temperature and elongation at superplastic temperature of the material reach HV469, 1 150 MPa and 632%, respectively, when the saccharin was used as additive.
Key words: additives; composites; mechanical properties; pulse current electrodeposition