aluminum alloy sheet under cyclic plastic deformation
（1. State Key Laboratory of Mechanical System and Vibration, Shanghai Jiao Tong University, Shanghai 200240, China;
2. Shanghai Key Laboratory of Digital Auto-body Engineering,
Shanghai Jiao Tong University, Shanghai 200240, China）
Abstract:A numerical analysis of mechanical behavior of aluminum alloy sheet under cyclic plastic deformation was investigated. Forming limit at fracture was derived from Cockcroft-Latham ductile damage criterion. The strain path of bending center of incremental roller hemming could be accepted as a kind of plane strain bending deformation process. Incremental rope roller hemming could be used to alleviate ductile fracture behavior by changing the stress state of the hemming-effected area. SEM observation on the fracture surface indicates that cyclic plastic deformation affects ductile fracture mechanism.
Key words: aluminum alloy; ductile damage; incremental forming; cyclic plastic deformation