中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 21 No. 2 February 2011 |
（1. College of Materials Science and Engineering, Chongqing University of Technology, Chongqing 400054, China;
2. National Engineering Research Center for Magnesium Alloys, Chongqing University, Chongqing 400044, China）
Abstract:A new severe plastic deformation (SPD) method that is extrusion-shearing (ES), which includes initial forward extrusion and shearing process subsequently, was developed to fabricate the fine grained AZ31 Mg alloys. The components of ES die were manufactured and installed to gleeble1500D thermo-mechanical simulator. Microstructure observations were carried out in different positions of ES formed rods. The results show that homogeneous microstructures with mean grain size of 2 μm are obtained at lower temperature as the accumulated true strain is 2.44. Occurring of continuous dynamic recrystallization (DRX) is the main reason for grain refinement during ES process. The experimental results show that the ES process effectively refines the grains of AZ31 magnesium. The production results of ES extrusion with industrial extruder under different extrusion conditions show that the ES extrusion can be applied in large-scale industry.
Key words: magnesium alloys; extrusion-shearing process; grain refinement; physical simulator
