Microstructure evolution and thixoextrusion of
AZ91D magnesium alloy produced by SSTT
CHENG Yuan-sheng(程远胜)1, CHEN Qiang(陈 强)2, HUANG Zhe-qun(黄哲群)1, HUANG Shu-hai(黄树海) 2

1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
2. Southwest Technique and Engineering Institute, Chongqing 400039, China

Abstract:The semi-solid thermal transformation (SSTT) route was used to obtain semi-solid billets for thixoextrusion. Microstructural evolution during partial remelting was studied. Mechanical properties of thixoextruded billets were determined. The results show that the solid grain size decreases initially and then increases as the isothermal holding time increases. Furthermore, shape factor measurements show that the solid grains tend to become increasingly spheroidal after 10 min isothermal holding. With longer isothermal holding time, the degree of spheroidization slightly decreases. Middle ultimate tensile strength (263.3 MPa) is obtained for thixoextruded AZ91D alloy produced by the SSTT route, with a yield strength of 120.0 MPa and an elongation to fracture of 7.19%.

 

Key words: AZ91D magnesium alloy; microstructure; semi-solid thermal transformation; thixoextrusion

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com