中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 20 No. 7 July 2010 |
ultrasonic processing
（1. Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China;
2. Key Laboratory for Advanced Materials Processing Technology of Ministry of Education,
Tsinghua University, Beijing 100084, China）
Abstract:Magnesium matrix nanocomposite reinforced with carbon nanotubes (CNTs/AZ91D) was fabricated by mechanical stirring and high intensity ultrasonic dispersion processing. The microstructures and mechanical properties of the nanocomposite were investigated. The results show that CNTs are well dispersed in the matrix and combined with the matrix very well. As compared with AZ91D magnesium alloy matrix, the tensile strength, yield strength and elongation of the 1.5%CNTs/AZ91D nanocomposite are improved by 22%, 21% and 42% respectively in permanent mold casting. The strength and ductility of the nanocomposite are improved simultaneously. The tensile fracture analysis shows that the damage mechanism of nanocomposite is still brittle fracture. But the CNTs can prevent the local crack propagation to some extent.
Key words: carbon nanotube; magnesium alloy; composite; ultrasonic processing