Vol. 6 No. 4 December 1996 |
(Institute of Metal Research, Chinese Academy of Sciences, Shenyang110015)
Abstract:A CVD SiC fibre-reinforced Ti-based composite was prepared by vacuum hot-press diffusion bonding technique. The SiC fibre has an amorphous carbon-rich surface coating of about 1μm in thickness. TEM observations showed that TiC and Ti3Si5 are formed in the interface region due to the reaction of SiC-Ti during the high temperature preparing process, but the amorphous carbon-rich layer of the fibre can be kept and the fibre-matrix can be bonded well if the fabricating parameters selected are reasonable. The room temeprature tensile strength and elastic modulus of SiCf(35% in volume)/Ti-15V-3Cr-3Sn-3Al composite are 1 284 MPa and 210 GPa respectively.
Key words: CVD SiC fibre β-Ti alloy vacuum hot press diffusion bonding technique SiCf/Ti composite