Abstract:The La-Mg-Ni system A₂B₇-type electrode alloys with nominal composition La_0.75−xZr_xMg_0.25Ni_3.2Co_0.2Al_0.1 (x=0, 0.05, 0.1, 0.15, 0.2) were prepared by casting and melt-spinning. The influences of melt spinning on the electrochemical performances as well as the structures of the alloys were investigated. The results obtained by XRD, SEM and TEM show that the as-cast and spun alloys have a multiphase structure, consisting of two main phases (La, Mg)Ni₃ and LaNi₅ as well as a residual phase LaNi₂. The melt spinning leads to an obvious increase of the LaNi₅ phase and a decrease of the (La, Mg)Ni₃ phase in the alloys. The results of the electrochemical measurement indicate that the discharge capacity of the alloys (x≤0.1) first increases and then decreases with the increase of spinning rate, whereas for x＞0.1, the discharge capacity of the alloys monotonously falls. The melt spinning slightly impairs the activation capability of the alloys, but it significantly enhances the cycle stability of the alloys.

Key words: A₂B₇-type electrode alloy; La-Mg-Ni alloy; Ni-MH battery; melt-spinning; electrochemical performance