Microstructure and mechanical properties of Mg-6Al-0.3Mn-xY alloys prepared by casting and hot rolling
SU Gui-hua(苏桂花), ZHANG Liang(张 亮), CHENG Li-ren(程丽任),
LIU Yong-bing(刘勇兵), CAO Zhan-yi(曹占义)

Key Laboratory of Automobile Materials, Ministry of Education,
Department of Materials Science and Engineering, Jilin University, Changchun 130025, China

Abstract:Mg-6Al-0.3Mn-xY (x=0, 0.3, 0.6 and 0.9, mass fraction, %) magnesium alloys were prepared by casting and hot rolling process. The influence of yttrium on microstructure and tensile mechanical properties of the AM60 magnesium alloy was investigated. The results reveal that with increasing the yttrium content, Al2Y precipitates form and the grain size is reduced. The ultimate strength, yield strength and elongation at room temperature are 192 MPa, 62 MPa and 12.6%, respectively, for the as-cast Mg-6Al-0.3Mn-0.9Y alloy. All these properties are improved obviously by hot rolling, and the values are up to 303 MPa, 255 MPa and 17.1%, respectively, for the rolled Mg-6Al-0.3Mn-0.9Y alloy. The improvement of mechanical properties is attributed to continuous dynamic recrystallization and the existence of highly thermal stable Al2Y precipitate which impedes the movement of dislocation effectively.

 

Key words: magnesium alloy; yttrium; hot rolling; dynamic recrystallization; mechanical properties

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com