ITO nano-powders prepared by microwave-assisted co-precipitation in
aqueous phase
ZHU Xie-bin(朱协彬), JIANG Tao(姜 涛), QIU Guan-zhou(邱冠周), HUANG Bai-yun(黄伯云)

School of Minerals Processing and Bioengineering, Central South University, Changsha 410083, China

Abstract:By using microwave-assisted co-precipitation in aqueous phase, adding surface activation agent PEG-6000 into the mixture of InCl3 solution and SnCl4 solution, and dropping the ammonia solution with the density (volume ratio) of 1׃0 to 1׃4, ITO precursor was prepared at different reaction system temperatures of 35 ℃−85 ℃, then ITO nano-powder was obtained after it was calcinated at 800 ℃for 1 h. The morphology of ITO nano-powder was characterized by SEM and its electrical conductivity was determined by conductivity meter. The effects of different temperatures and ammonia concentration in microwave-assisted reaction system on its morphology and electric conductivity were discussed. The experimental results indicate that with the dilution of the ammonia solution or the rise of reacting system temperature, the morphology of ITO particles is transformed from spherical to rod-like one with the decline of its electric conductivity. And the electric conductivity of ITO nano-powders with spherical morphology is higher than that of ITO nano-powders with rod-like morphology.

 

Key words: ITO nano-powder; surface activation agent PEG-6000; microwave assistance; co-precipitation; aqueous phase

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com