Nanostructured Al-Zn-Mg-Cu alloy synthesized by cryomilling and
spark plasma sintering
CHEN Han-bin(陈汉宾)1, TAO Kai(陶 凯)2, YANG Bin(杨 滨)2, ZHANG Ji-shan(张济山)

1. No.59 Institute of China Ordnance Industry, Chongqing 400039, China;
2. State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing,
Beijing 100083, China

Abstract:Nanocrystallized Al-10.0%Zn-3.0%Mg-1.8%Cu (mass fraction) alloy powder was prepared by cryomilling, and then the nanostructured powder was consolidated into bulk material by spark plasma sintering (SPS). The microstructural evolution and phase transformation were studied. A supersaturated face-centered cubic solid solution is formed after cryomilling for 10 h, and the average grain size is 28 nm. Two typical nanostructures of the bulk nanostructured alloy are observed:primarily equiaxed grains with size of 150 nm, and occasionally occurring sub-micron grains up to 500 nm. Two types of MgZn2 particles precipitate during consolidation. One is the sub-micron particles distributed along the boundaries of the powders, and the other is fine particles with size of several nanometers in the matrix, especially at the boundaries of sub-micron grains. These second phase particles can be completely dissolved into matrix by proper solid solution treatment.

 

Key words: cryomilling; spark plasma sintering; nanostructured Al-Zn-Mg-Cu alloy; microstructural evolution; second phase

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com