中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
Vol. 12 No. 6 December 2002 |
(1. Department of Mechanical Engineering,
Northern Jiaotong University,Beijing 100044, China;
2. Department of Mechanical Engineering,
Tsinghua University, Beijing 100084, China;
3. Metal Forming Department, Northeastern University, Shenyang 110006, China;
4. Anshan Automobile Fittings Factory,Anshan 114014, China)
Abstract:The bonding of steel plate to Al-7graphite slurry was conducted using casting rolling technique. The influence of diffusion time on interfacial mechanical property and structure of bonding plate was studied. The results show that: under the condition of 510℃ for preheat temperature of steel plate and 32% of solid fraction of Al-7 graphite slurry, the relationship between interfacial shear strength S and diffusion time t is S=25.3+4.47t-0.133t2+0.001t3. When diffusion time is 22.5s, the largest interfacial shear strength 69.9MPa is got, and the corresponding interface is made up of Fe-Al compound and Fe-Al solid solution alternatively and in a right proportion.
Key words: diffusion time; interfacial shear strength; interfacial structure