Temperature dependence of deformation mechanism in single crystal Ni-base superalloy
ZHANG Xuan(张 炫), JIN Tao(金 涛), ZHAO Nai-ren(赵乃仁), 
WANG Zhi-hui(王志辉), SUN Xiao-feng(孙晓峰), 
GUAN Heng-rong(管恒荣), HU Zhuang-qi(胡壮麒)

Department of Superalloys, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

Abstract: The tensile behavior of a new single crystal Ni-base superalloy was studied at various temperatures. Specimens were strained to fracture in the temperature range from 20℃ to 1000℃. σ0.2 is essentially unaffected by temperatures between 20℃ and 400℃. At higher temperatures it increases until it reaches a maximum at about 800℃. Beyond 800℃ a sharp decrease of strength is observed. There is a slight fluctuation in ductility between 20℃ and 800℃. The elongation to fracture increases from 10% to 36% as the temperature increases from 800℃ to 1000℃. The deformation is dominated by γ′ shearing and the high-density dislocations are observed in matrix channels at low temperatures. The dislocation microstructure is inhomogeneous due to the formation of dislocation concentrations with high-density tangling at intermediate temperatures. The networks deposited at the γ/γ′ interfaces prevent dislocations from entering the γ′ precipitates at high temperatures.

 

Key words: single crystal; Ni-base superalloy; tensile; microstructure; dislocation

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com