Effect of hot extrusion on microstructure and mechanical properties of quasicrystal-reinforced Mg-Zn-Y alloy
ZHENG Ming-yi(郑明毅)1, QIAO Xiao-guang(乔晓光)1
XU Shi-wei(徐世伟)1, GAN Wei-min(甘为民)1, WU Kun(吴昆)1
S.Kamado2

1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China; 
2. Department of Mechanical Engineering, Nagaoka University of Technology, 
Nagaoka 940-2188, Japan; 
3. Institute of Materials Engineering, GKSS-Research Center, D21502, 
Geesthacht, Germany

Abstract: The microstructure and mechanical properties of as-cast and as-extruded Mg-Zn-Y alloy (Mg-11%Zn-0.9%Y, mass fraction) containing Mg3YZn6 quasicrystal were studied. The eutectic icosahedral quasicrystal phase (I-phase) is broken and almost distributes along the extrusion direction, and fine I-phase with nano-size is precipitated during the extrusion. The α-Mg matrix grains are refined due to recrystallization occuring during the hot extrusion. Some {10(-1)2} twins are observed in the extruded ZW1101 alloy. And {0002}〈10(-1)0〉 fiber texture is formed in matrix alloys after hot extrusion. The extruded alloy exhibits high strength in combination with large elongation at room temperature. The strengthening mechanism of the as-extruded alloy was discussed.

 

Key words:  magnesium alloys; quasicrystal; extrusion; microstructure; mechanical properties

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com