中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 15 No. 1 February 2005 |
（1. School of Physics Science and Technology, Central South University,
Changsha 410083, China;
2. School of Materials Science and Engineering, Central South University,
Changsha 410083, China）
Abstract:The microstructures and the tensile mechanical properties in the rolling plane of 1545 aluminum alloy sheet at different orientations with respect to the rolling direction were studied by means of tensile test, X-ray diffractometer(XRD), optical microscope and transmission electron microscope. The in-plane anisotropy of tensile mechanical properties was calculated and the inverse pole figures of the rolling plane, transversal section and longitudinal section were obtained by Harris method. The results show that the 1545 Al alloy sheet has remarkable in-plane anisotropy of mechanical properties and the main texture component is {110}〈112〉 texture. On the basis of the model that regards the sheet containing only {110}〈112〉 texture as a monocrystal, the relationship of in-plane anisotropy and the anisotropy of crystallography was analyzed. The study shows that it is the combined effects of the anisotropy of crystallography and microstructures that cause the in-plane anisotropy of mechanical properties, but the main cause is the crystallographic texture.
Key words: 1545 alloy aluminum sheet; in-plane anisotropy; inverse pole figure; crystallographic texture