Effect of rod-like grain on properties and toughening mechanism of 3Y-TZP/Al2O3 ceramics
RONG Shou-fan(荣守范)1, 2, JI Ze-sheng(吉泽升)1, ZHU Yong-chang(朱永长)2, ZHANG Jing-qiang(张敬强)2

1. School of Materials Science and Technology, Harbin University of Science and Technology,Harbin 150040, China;2. School of Materials Science and Technology, Jiamusi University, Jiamusi 154007, China

Abstract:In-situ rod-like Al2O3 grain was prepared by adding CAS multiphase additives under the sintering condition of 30 MPa, 1 550 ℃ and 1 h. The sintering behaviors, microstructure, toughening mechanism and access of Al2O3 ceramics were investigated by SEM, EDS and WDW omnipotent electronic mechanical testing machine, etc, and the crack propagating model of cylindrical crystal/3Y-TZP composite toughening Al2O3 ceramics was established. The results show that the composite additives prompt the anisotropic growth of Al2O3 grain, which strengthens toughening effect of 3Y-TZP in 3Y-TZP/Al2O3 composite ceramics. Moreover, the experimental material density is near to theoretical density, bending strength is 556.35 MPa, and fracture toughness is 6.73 MPa•m1/2. The mechanical properties of the materials are obviously improved.


Key words: rod-like grain; multitoughening; additives; Al2O3; microstructure; mechanical properties

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱