中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
Vol. 18 No. 4 August 2008 |
(1. School of Metallurgical Science and Engineering, Central South University, Changsha 410083, China;
2. Shandong Branch, China Aluminum Corporation, Zibo 255052, China)
Abstract:The thermal stability, particle size and morphology and oil absorption of aluminum hydroxide(ATH) treated by dry modification with three different modifiers were investigated. The experimental results show that the thermal stability of ATH powder is markedly improved by dry modification technology with the following modifiers such as phosphoric acid, polyacrylic acid and the mixture of phosphoric acid and polyacrylic acid. The best effect comes from pure phosphoric acid, and the initial temperature for the loss of crystal water of ATH powder modified with pure polyacrylic acid can reach about 202 ℃ that is approximately 10 ℃ higher than that of ATH powder before modification. The phenomena of agglomeration and macro-aggregate badly exist in ATH powder modified with the modifiers containing phosphoric acid. The growth of particles and agglomerations of powders are not evident in ATH powder modified with pure polyacrylic acid. The oil absorption of ATH powder modified with the modifiers containing phosphoric acid is apparently larger than that of original ATH powder and ATH powder modified with pure polyacrylic acid. The oil absorption of the ATH powder modified with pure polyacrylic acid is slightly smaller than that of original ATH powder.
Key words: aluminum hydroxide; dry modification; polyacrylic acid; thermal stability; oil absorption