中国有色金属学报(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 17 No. 6 December 2007 |
（National Engineering Research Center of Light Alloys Net Forming, School of Materials Science and Engineering, Shanghai Jiao Tong University,Shanghai 200030, China ）
Abstract:The corrosion behaviour of Mg-3.0Nd-0.4Zr (NK30) magnesium alloy was investigated in as-cast (F), solution treated (T4) and peak-aged (T6) conditions in 5% NaCl solution by immersion tests and electrochemical measurements. The results of immersion test show that NK30 alloy exhibits better corrosion resistance in F condition than it does in the other two conditions due to the more compact corrosion film formed on alloy in F condition. The potentiodynamic polarization curves show that the overpotential of cathodic hydrogen evolution reaction on NK30-F is much higher than that on NK30-T4 and NK30-T6. The corrosion potentials of NK30 increase in the following order: F＜T4＜T6. The results of electrochemical impedance spectroscopy (EIS) also confirm that the corrosion film of NK30-F plays a more protective role than that of NK30-T4 and NK30-T6.
Key words: Mg-Nd-Zr alloy; corrosion behaviour; heat treatment; potentiodynamic polarization; electrochemical impedance spectroscopy