Residual stress distribution in different depths of TiNi/Ti2Ni-based laser clad coating prepared at different environmental temperatures
Yang-feng TAO, Jun LI, Ying-hao Lü, Lie-feng HU

School of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620, China

Abstract:This study aimed to effectively reduce the cracking susceptibility of the laser clad coating by enhancing the environmental temperature during laser cladding, and reveal the residual stress distribution in different depths of the coating. The TiNi/Ti2Ni-based coatings were prepared on Ti6Al4V by laser cladding at different environmental temperatures of 25, 400, 600 and 800 °C. The changes in residual stress along the depth of the coatings were investigated in detail by the nanoindentation method. Results showed that the average residual stress of 2.90 GPa in the coating prepared at 25 °C was largest. With the increase in environmental temperature, the average residual stress was reduced to 1.34 GPa (400 °C), 0.70 GPa (600 °C) and 0 GPa (800 °C). For all the coatings, the residual stress was increased with increasing the distance from the coating surface. Enhancing the environmental temperature can effectively reduce the cracking susceptibility of the coatings.

 

Key words: laser cladding; coating; microstructure; environmental temperature; cracking susceptibility; residual stress; nanoindentation

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f-ysxb@mail.csu.edu.cn