Influence of adipic acid on anodic film formation and corrosion resistance of 2024 aluminum alloy
Ying-dong LI1,2, You ZHANG1, Song-mei LI1, Pi-zhi ZHAO2

1. School of Materials Science and Engineering, Beihang University, Beijing 100191, China;
2. Chinalco Research Institute of Science and Technology Co., Ltd., Beijing 102209, China

Abstract:The influence of adipic acid on the formation and corrosion resistance of anodic oxide film fabricated on 2024 aluminum alloy was investigated. The morphology was investigated by scanning electron microscopy (SEM) and transmission electron microscopy (TEM), respectively. The corrosion resistance was evaluated by electrochemical impedance spectroscopy (EIS). The results showed that the adipic acid was absorbed at the electrolyte/anodic layer interface during anodizing. The corrosion rate of anodic film decreased and the film thickness increased. The film was uniform and compact especially at the film/substrate interface. After sealing procedure, anodic film formed with the addition of adipic acid exhibited improved dielectric property and corrosion resistance in aggressive environment.

 

Key words: aluminum alloy; anodic oxidation; adipic acid; adsorption; corrosion

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f-ysxb@mail.csu.edu.cn