Effects of Ti and Be addition on microstructure and mechanical properties of Mg58.5Cu30.5Y11 bulk metallic glass
Ke-qiang QIU, Lin WANG, Ying-lei REN, Rong-de LI

School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China

Abstract:Based on the Mg58.5Cu30.5Y11 alloy, 10% Ti, 10% Be and 10% Ti70Be30 (mole fraction) were respectively added to the alloy and samples with a diameter of 3 mm were fabricated by conventional Cu-mold casting method. The phase constituent, thermal stability and microstructure of the alloys were investigated by using X-ray diffraction, differential scanning calorimetry and scanning electron microscopy, respectively. The effects of alloying elements Ti and Be on the microstructure and mechanical properties of Mg58.5Cu30.5Y11 alloy were discussed. The results show that CuTi phase is distributed in (Mg0.585Cu0.305Y0.11)90Ti10 and (Mg0.585Cu0.305Y0.11)90(Ti0.7Be0.3)10 alloys, while CuYBe glassy phase containing CuY crystals is embedded in the matrix of (Mg0.585Cu0.305Y0.11)90Be10 alloy. Under uniaxial compressive loading, the largest compressive fracture strengths for (Mg0.585Cu0.305Y0.11)90Ti10, (Mg0.585Cu0.305Y0.11)90Be10 and (Mg0.585Cu0.305Y0.11)90(Ti0.7Be0.3)10 alloys are 797.6, 952.6 and 1007.8 MPa, respectively, and the strengths are increased by about 17%, 40% and 48% compared with Mg58.5Cu30.5Y11 alloy. The strength reliability for the three alloys is much improved according to the strength distribution region of 10 samples of each alloy.


Key words: Mg-based alloy; alloying element; Ti; Be; microstructure; strength reliability

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱