Microstructures and mechanical properties of laser welded wrought fine-grained ZK60 magnesium alloy
Hong-ge YAN1,2, Qiang ZHAO1,2, Ping CHEN1,2, Ji-hua CHEN1,2, Bin SU1,2

1. School of Materials Science and Engineering, Hunan University, Changsha 410082, China;
2. Hunan Provincial Key Laboratory of Spray Deposition Technology and Application,
Hunan University, Changsha 410082, China

Abstract:Fine-grained ZK60 magnesium alloy sheets of 2.0 mm in thickness were successfully joined by laser beam welding (LBW). The effects of welding parameters including laser power and welding speed on the microstructures and mechanical properties of the joints were investigated. A sound bead, with the ultimate tensile strength (UTS) of 300 MPa and elongation of 12.0%, up to 92.5% and 65% of those of the base metal, respectively, is obtained with the optimized welding parameters. No liquation cracking is visible in the partially melted zone (PMZ) owing to the inhibitory action of the fine dispersed precipitates and the fine-grained microstructure in the as-rolled magnesium alloy sheets. The fusion zone (FZ) is featured with the equiaxed dendritic grains of the average grain size about 8 μm, which are similar to those in the heat affected zone (HAZ), and this contributes to the relatively high joint efficiency.

 

Key words: ZK60 magnesium alloy; fine grain size; laser beam welding; heat affected zone; partially melted zone

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com