热处理制度对Mg-Y-Al-Si-O-N玻璃析晶行为的影响
李秀英,卢安贤

(中南大学 材料科学与工程学院,长沙 410083)

摘 要: 分别研究核化温度、核化时间和晶化温度对Mg8.88Y5.92Al10.15Si15.22O52.65N7.19(摩尔分数,%)氧氮玻璃析晶行为的影响。此外,还对比研究了两步和一步热处理制度对此玻璃析晶行为的影响。用DSC曲线初步确定玻璃成核和晶化温度范围,再用传统方法确定玻璃的最佳热处理制度;用X-射线衍射仪鉴定微晶玻璃中的物相;用扫描电镜观察微晶玻璃的微观结构。结果表明:对于此组成玻璃,热处理制度严重影响微晶玻璃的析晶度和微观形貌,但对析出相的种类影响较小;所制备的微晶玻璃中均含YMgSi2O5N(48-1632)、MgSiO3(19-0768)和Mg3Al2(SiO4)3 (15-0742)相,其中YMgSi2O5N为主晶相,呈棒状。

 

关键字: 热处理制度;Mg-Y-Al-Si-O-N玻璃;晶相;析晶度;显微结构

Effects of heat treatment schedule on crystallization behaviors of Mg-Y-Al-Si-O-N glasses
LI Xiu-ying, LU An-xian

School of Materials Science and Engineering, Central South University, Changsha 410083, China

Abstract:A glass with the composition of Mg8.88Y5.92Al10.15Si15.22O52.65N7.19 (in mole fraction, %) was chosen as parent glass. The influence of nucleation temperature, nucleation time and crystallization temperature on the crystallization behavior of this glass was studied. Furthermore, the effect of one-stage heat treatment on the crystallization behavior of this glass was also investigated in comparison with two-stage heat treatment. The temperature ranges for nucleation and crystallization were both determined by DSC curve of the glass. Based on the DSC curve, the optimum heat treatment schedule was determined by classical method. The crystalline phases in the glass-ceramics were identified by X-ray diffraction. The microstructures of the glass-ceramics were observed by scanning electron microscopy. The results indicate that for this glass, heat treatment has great effects on volume fraction of the crystalline phases and the microstructures of the glass-ceramics, whereas the effect on the type of the crystalline phases precipitated is small. All glass-ceramics contain YMgSi2O5N(48-1632), MgSiO3(19-0768) and Mg3Al2(SiO4)3(15-0742) phases. Rod-shape YMgSi2O5N as the dominant phase appears in all glass-ceramics.

 

Key words: heat treatment schedule; Mg-Y-Al-Si-O-N glasses; crystalline phase; volume fraction of crystalline phases; microstructure

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f-ysxb@mail.csu.edu.cn