FGH95高温合金的静态再结晶机制
胡本芙1, 陈焕铭1, 2, 金开生1, 李慧英1

( 1. 北京科技大学 材料科学与工程学院, 北京 100083; 
2. 宁夏大学 物理与电气信息工程学院, 银川 750021
)

摘 要: 对热等静压FGH95合金高温挤压形变后的试样进行静态再结晶处理,讨论了其再结晶形核机制及γ′相对再结晶过程的影响。 结果表明: 合金在γ′相几乎完全溶解温度以上再结晶时, 形核以应变诱发晶界迁移机制进行, 而在γ′相大量存在的温度范围内则是以亚晶粗化形核机制进行; γ′相的分解速率对再结晶速率有重要影响,随再结晶温度的升高, γ′相分解速率加快, 再结晶激活能减小, 再结晶速率加快, γ′相分解后以同步或不同步方式重新析出。

 

关键字: FGH95高温合金;静态再结晶; 形核机制

Static recrystallization mechanism of FGH95 superalloy
HU Ben-fu1, CHEN Huan-ming1, 2
JIN Kai-sheng1, LI Hui-ying1

1. School of Materials Science and Engineering,
University of Science and Technology Beijing, Beijing 100083, China;
2. School of Physics and Electrical Information Engineering,Ningxia University,
 Yinchuan 750021, China

Abstract: The as-HIPed FGH95 alloy was deformed by extrusion at high temperature, and then the as-extruded sample was treated with static recrystallization. The nucleation mechanism and the influence of γ′ phase on recrystallization process during static recrystallization were also discussed. The results indicate that the nucleation mechanism is strain-induced boundary migration (SIBM) when alloy is treated near the temperature at which γ′ phase can be dissolved completely, and it is sub-grain coalescence when alloy is treated at the temperature at which a lot of γ′ phase exist. The γ′ phase decomposition rate has an important influence on the recrystallization rate. With the recrystallization temperature increasing, the γ′ phase decomposition rate increases and the activation energy of recrystallization decreases, resulting in recrystallization rate to increase. The γ′ phase re-precipitates in recrystallized grains by synchronization or non-synchronization.

 

Key words: FGH95 superalloy; static recrystallization; nucleation mechanism

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f-ysxb@mail.csu.edu.cn