Undercooling heredity of Cu70Ni30melt solidified in
non-catalytic nucleation coated mould①
GUO Xue-feng(郭学锋)1,2, LIU Yong-chang(刘勇长)2,
YANG Gen-cang(杨根仓)2, XING Jian-dong(邢建东)1

1. School of Mechanical Engineering, Xi′an Jiaotong University, Xi′an 710049, P.R.China;
2. State Key Laborotary of Solidification Processing, Northwestern Polytechnical University,
Xi′an 710072, P.R.China

Abstract:A new concept of undercooling heredity is developed to evaluate the undercooling ability in a non-catalytic nucleation coated mould, where alloy melts were highly undercooled previously. Before the heredity experiment a noncatalytic nucleation composite glass-lined coating (B-F) was prepared on the inner surface of mould and the Cu70Ni30alloy was selected to perform undercooling experiment in the B-F non-catalytic coating mould. Its ratio of undercooling heredity
was 0.76. The results prove that the B-F coating is an ideal non-catalytic media for purified Cu70Ni30alloy melts due to its small contact angle between the melt and coating layer. Considering that various microstructures form under different undercoolings, two critical undercoolings,ΔT1andΔT2, and their corresponding microstructures of Cu70Ni30alloy are well defined. Moreover, it is found that the manned-trigging solidification in the non-catalytic coating mould could be used to get directional undercooling dendrite structure while the melt undercooling is larger than the critical undercoolingΔT2.


Key words: Cu70Ni30alloy; non-catalytic nucleation coating; undercooling heredity

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱