Characteristics of electrodeposited RE-Ni-W-B-B4C-MoS2 composite coating
MA Ke-yi(马克毅), GUO Zhong-cheng(郭忠诚),
ZHU Xiao-yun(朱晓云), XU Rui-dong(徐瑞东)

Faculty of Materials and Metallurgical Engineering,
Kunming University of Science and Technology, Kunming 650093, China

Abstract:The high temperature oxidation resistance of RE-Ni-W-B-B4C-MoS2 composite coating, the effects of electrodeposition conditions on the morphologies of the coating and the effect of heat treatment temperature on its hardness, abrasion resistance and phase structure were investigated by using scanning electron microscope(SEM), X-ray diffractometer, microhardness tester and abrasion machine. The results show that the oxidation degree of RE-Ni-W-B-B4C-MoS2 composite coating is small when the temperature is lower than 700℃, but it increases sharply when the temperature is higher than 700℃. The hardness of RE-Ni-W-B-B4C-MoS2 composite coating increases with increasing heat treatment temperature, it comes up to the maximum value at 400℃, but it decreases gradually if the temperature rises continuously. The most favourable abrasion resistance was attained after RE-Ni-W-B-B4C-MoS2 composite coating being heat treated at 400℃. Without heat treating, it is mainly amorphous and partially crystallized, but wholly crystallized after being heat treated at 500℃. RE in the composite coating is in the form of CeO2 and additions of CeO2 and B4C can enhance the thermostability of RE-Ni-W-B-B4C-MoS2 composite coating.


Key words: electrodeposition; RE-Ni-W-B-B4C-MoS2 composite coating; characteristics

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱