Effect of rolling on interfacial property of steel/mushy Al-20Sn bonding plate
ZHANG Peng(张 鹏)1, DU Yun-hui(杜云慧)1,
LIU Han-wu(刘汉武)1, ZENG Da-ben(曾大本)2,
CUI Jian-zhong(崔建忠)3, BA Li-min(巴立民)4

1. Department of Mechanical Engineering, Northern Jiaotong University, Beijing 100044, China;
2. Department of Mechanical Engineering,
Tsinghua University, Beijing 100084, China;
3. Metal Forming Department, Northeastern University,
Shenyang 110004, China;
4. Anshan Automobile Fittings Factory, Anshan 114014, China

Abstract:The rolling treatment of steel/mushy Al-20Sn bonding plate was conducted under different relative reduction at room temperature. The effect of room-temperature rolling on interfacial mechanical property of bonding plate was studied. The results show that, for steel/mushy Al-20Sn bonding plate which consists of 1.2mm-thick 08Al steel plate and 2.0mm-thick Al-20Sn layer, the relationship between interfacial shear strength and relative reduction is S=70.1+5.48r-r2(S is interfacial shear strength, r is relative reduction). When the relative reduction is 2.74%, the largest interfacial shear strength 77.6MPa can be obtained.

 

Key words: rolling; relative reduction; interfacial shear strength

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com