Synthesis and characterization of metastable Ag-B solid solutions
ZHANG Jiang(张 弜)1, LI Zong-quan(李宗全)1,2, SHA Jian(沙 健)3

1. Department of Materials Science and Engineering,
Zhejiang University, Hangzhou 310027, China;
2. State Key Laboratory of Silicon Materials,
Zhejiang University, Hangzhou 310027, China;
3. Department of Physics, Zhejiang University, Hangzhou 310027, China

Abstract:Mechanical alloying (MA) was applied to Ag-B immiscible binary systems by ball milling elemental Ag and B powders. The microstructural characterization of the milled powders was carried out by XRD and TEM. The results show that face-centered-cubic (FCC) Ag-B solid solutions are formed and that the maximum ratio of B to Ag is 4∶1. The structure evolution of Ag-B solid solution during ball milling indicates that the formation of Ag-B solid solution may be divided into two stages, which are mainly substitutional and interstitial solutions separately. The decomposition of the as-milled granules under the irradiation of electron beam is observed by TEM, which reveals that the solid solutions are metastable.

 

Key words: mechanical alloying; Ag-B solid solution; metastable.

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com