Corrosion behavior of NiCr alloys
in HCl-containing oxidation atmosphere at 700 800℃
ZHANG Ke(张 轲), NIU Yan(牛 焱), PAN Tai-jun(潘太军), WU Wei-tao(吴维山文)

State Key Laboratory for Metals Corrosion and Protection, Institute of Metal Research,
Chinese Academy of Sciences, Shenyang 110016, China

Abstract:Corrosion behaviors of pure Ni and three NiCr alloys were investigated in an HCl-containing oxidizing atmosphere at 700℃and 800℃. All materials suffer from accelerated corrosion at both temperatures. NiCr alloys show an initial mass loss due to the formation of volatile CrCl3and CrO2Cl2. Some chlorides are detected at the scale/substrate in terface and many voids are also found there. NiCr alloys with higher chromium content have better corrosion resistance.However, Ni50Cr is inferior to Ni25Cr due to its two-phase structure, which makes it easy for chlorine to diffuse along grain boundary and to occur inner oxidation. The relevant corrosion mechanism was also discussed.

 

Key words: NiCr alloy; high temperature corrosion; refuse incineration; chlorination-oxidation; active oxidation

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f-ysxb@mail.csu.edu.cn