Effects of rapid heating cyclic heat treatment on microstructures and
compression mechanical properties of TiAl-based alloy
PENG Chao-qun(彭超群)1, HE Yue-hui(贺跃辉)1, HUANG Bai-yun(黄伯云)1, P.K.Liaw2

1. State Key Laboratory for Powder Metallurgy, Central South University, Changsha 410083, China;
2. Materials Science and Engineering Department, University of Tennessee,
Knoxville, TN 37996-2200, USA

Abstract:By means of rapid heating cyclic heat treatment, the microstructure of a TiAl-based alloy was refined. The colony size and lamellar spacing were measured to be 50μm and 0.12μm, respectively. The compression mechanical properties were determined at room temperature and the best comprehensive mechanical properties can reachσ0.2of 745.1 MPa,σpof 1 672.2 MPa andδof 19.40%. The improvement of mechanical properties is caused by the microstructural
refinement and the phase interface nucleation contributes a lot to the refinement of microstructure.


Key words: TiAl; compression mechanical properties; microstructural refinement; phase interface nucleation

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱