Microstructure and properties of 7A52 Al alloy welded joint
HUANG Ji-wu(黄继武)1, 2, YIN Zhi-min(尹志民)1, LEI Xue-feng(雷学锋)1, 3

1. School of Materials Science and Engineering, Central South University, Changsha 410083, China;
2. Key Laboratory of Nonferrous Metal Materials Science and Engineering, Ministry of Education,
Central South University, Changsha 410083, China;
3. Aerospace Research Institute of Materials and Processing Technology, Beijing 100076, China

Abstract:7A52 Al alloy plate aged at 105 ℃ for 8 h and then at 130 ℃ for 24 h was welded by means of TIG using Al- 6.3Mg-0.35Sc-0.1Zr-0.1Cr solder wire. Mechanical properties and microstructures of welded joint were studied. There are two obviously soft areas in the welded joint, welding seam and over-aging zone. The mechanical properties of welded joint are that σb is 358 MPa, σ0.2 is 238 MPa and δ5 is 6.6%. 75.6% of welding coefficient can be achieved. The addition of scandium leads to very significant grain refinement in the fusion zone, which results in a reduction in solidification cracking tendency. The solidification cracking isn’t observed.

 

Key words: microalloying; Al alloy; welded joint; microstructure; mechanical properties

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f-ysxb@mail.csu.edu.cn