Synthesis of Ti2AlC by hot pressing andits mechanical and electrical properties
WANG Ping(王 苹)1, 2, MEI Bing-chu(梅炳初)2, HONG Xiao-lin(洪小林)2, ZHOU Wei-bing(周卫兵)2

1. School of Science, Wuhan University of Technology, Wuhan 430070, China; 2. State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, China

Abstract:Ti2AlC bulk material was synthesized by hot pressing of mixture powders of TiC, Ti, Al and active carbon. The phase compositions of resultant product at different temperature were detected by X-ray diffractometer. The microstructures of the samples were observed by SEM. Finally, the mechanical properties and thermal properties of the sample at 1 400 ℃ were measured. The results show that high purity Ti2AlC material with little Ti3AlC2 can be synthesized by hot pressing 0.5TiC/1.5Ti/1.0Al/0.5C at 1 400 ℃. Ti2AlC exhibits high mechanical properties and metallic electrical properties. Its fracture toughness is 7.0 MPa∙m1/2, its flexural strength is 384 MPa at room temperature, and its electrical conductivity is 2.56×106 Ω−1∙m−1 at room temperature.

 

Key words: hot pressing; Ti2AlC; mechanical properties; electrical properties

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f-ysxb@mail.csu.edu.cn