Structure and transport properties of (La1−x−yYy)2/3Ca1/3MnO3 with La-site vacancies
LUO Guang-sheng(罗广圣)1, 2, LIU Guang-hua(刘光华)2, LI Xiao-yi(李小怡)2, XIONG Wei-hao(熊惟皓)1, WU Xiao-shan(吴小山)3

1. School of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China; 2. School of Materials Science and Engineering, Nanchang University, Nanchang 330031, China; 3. Laboratory of Solid State Microstructures, Nanjing University, Nanjing 210093, China

Abstract:Several samples of manganese oxides La(1−x)2/3Ca1/3MnO3 (V-LCMO) and (La0.7−xY0.3)2/3Ca1/3MnO3 (x<0.15) (V-LYCMO) with vacancies at La-site (La-vacancy) were prepared by solid-state reaction method. The X-ray diffraction(XRD) patterns refined by Rietveld confirm that these compounds exhibit single phase structure with orthorhombic symmetry (Pnma). The lattice parameters, Mn—O bond length and Mn—O—Mn bond angle vary with La-vacancy concentration, as an indication of the occurrence of the local Jahn-Teller effect. The measurement result of V-LCMO compounds shows that the maximum magnetoresistance(MR) is about 220% at TIM=268 K and La-vacancy content x=0.04. For V-LYCMO compounds, there exists metal-insulator transition at about 50 K, and a very large MR (over 106%) is observed at the temperature ranging from 40 K to 50 K.

 

Key words: La(1−x)2/3Ca1/3MnO3; (La0.7−xY0.3)2/3Ca1/3MnO3; La-vacancy; orthorhombic symmetry; Jahn-Teller effect

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f-ysxb@mail.csu.edu.cn