高硅氧化锌矿加压酸浸处理
李存兄,魏  昶,樊  刚,杨秀丽,徐红胜,邓志敢,李旻廷,李兴彬

(昆明理工大学 冶金与能源工程学院,昆明 650093)

摘 要: 通过对广西某地高硅氧化锌矿矿物分析可知,矿物中的锌主要以硅锌矿和异极矿的形式存在。采用加压酸浸技术对该高硅氧化锌矿进行处理,条件试验研究得出最佳工艺条件为:矿物粒度0.104 mm,硫酸浓度120 g/L,釜内压力1.0 MPa,浸出时间90 min,反应温度120 ℃,液固比3׃1。综合性试验研究得出:在最佳工艺条件下,锌浸出率可达97%以上,SiO2截留率大于99.2%,浸出矿浆过滤速率大于880 L/(m2·h),浸出矿浆具有良好的过滤性能。

 

关键字: 高硅氧化锌矿;加压酸浸;锌浸出率;SiO2截留率;矿浆过滤性能

Pressure acid leaching of high silicon zinc oxide ore
LI Cun-xiong, WEI Chang, FAN Gang, YANG Xiu-li, XU Hong-sheng, DENG Zhi-gan, LI Min-ting, LI Xing-bin

College of Metallurgical and Energy Engineering, Kunming University of Science and Technology,
 Kunming 650093, China

Abstract:According to the mineral analysis of high silicon zinc oxide ore from Guangxi province, most of zinc exists in matters of zinc silicate and calamine. The ore was treated by oxygen pressure acid leaching. The best technology conditions are obtained by condition experiments, which are particle size 0.104 mm, sulfuric acid 120 g/L, oxygen pressure 1.0 MPa, leaching time 90 min, reacting temperature 120 ℃ and liquid solid ratio of 3:1. It can be concluded that under the best technology conditions, the leaching rate of zinc is 97% and the rate of SiO2 in solid form is above 99.2%, the slurry filtration rate is over 880 L/(m2·h) and the leaching slurry is in good filtration property.

 

Key words: high silicon zinc oxide ore; pressure acid leaching; leaching rate of zinc; rate of SiO2 in solid form; filtration property of slurry

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com