AM60变形镁合金薄板激光焊接
接头的组织与性能
全亚杰, 陈振华, 黎 梅, 俞照辉, 龚晓叁

(湖南大学 材料科学与工程学院, 长沙 410082)

摘 要: AM60变形镁合金薄板为研究对象,分析CO2激光焊后接头的组织和性能,探讨镁合金激光焊接的工艺特点。结果表明:在合适的工艺参数下,能获得表面成型良好、变形小的焊接接头。金相观察分析发现接头中热影响区不明显,焊缝区组织致密,晶粒细小,晶界上均匀分布着脆性相(Mg17Al12),但内部易产生气孔、裂纹等微观缺陷。硬度测试结果显示,焊缝硬度略高,母材和热影响区硬度相当。在本实验条件下采用CO2激光焊能实现AM60镁合金的焊接,抗拉强度可达母材的94%,断口表现为混合断裂。

 

关键字: 变形镁合金AM60;激光焊接;微观组织;力学性能

Microstructure and properties of joints of
wrought magnesium alloy
AM60 plates welded by laser beam welding
QUAN Ya-jie, CHEN Zhen-hua, LI Mei, YU Zhao-hui, GONG Xiao-san

School of Materials Science and Engineering, Hunan University,Changsha 410082, China

Abstract:The CO2 laser beam was used to weld the wrought magnesium alloy AM60 plates, the microstructure and mechanical properties of the joints were studied, and the technical characteristics of magnesium alloy laser welding were discussed. The results show that a favorable weld without obvious distortion can be obtained under the suitable parameters. By metallurgical analysis it is found that the heat affected zone is not distinct, and the microstructure in fusion zone presents compact fine grains with brittle intergranular precipitates (Mg17Al12), which often accompanies with micro defects such as porosity and cracking. The result of hardness test shows that the hardness of the weld is slightly high, while the hardness of the base metal is equivalent to that of the HAZ. Under this experimental condition, the wrought magnesium alloy AM60 can be welded by CO2 laser beam welding, and the joint strength is up to 94% of the base metal. The fracture surface is characterized by mixture fracture.

 

Key words: wrought magnesium alloy AM60; laser beam welding; microstructure; mechanical property

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com